PRODUCT DESCRIPTION:
Fiber-Optic-Bond 23, High Temp Epoxy Adhesive, Fast Cure, Low Visc, 2 Part, Fiber Optic Connectors is a low viscosity, two-component epoxy formulation that signals both proper mixing and curing when bonding fiber optic bundles, potting glass fibers, and/or terminating single or multi-channel fiber optic connectors. Although this unique three-step color-change formulation unmixed components are light yellow, it turns light green on mixing, and changes again to a deep reddish-amber after the REQUIRED 100C HIGH TEMPERATURE CURE. It exhibits good wicking, and develops strong, tough, mechanically stable bonds to a wide variety of fiber optic and optical materials that includes most metals, ceramics, glass and many plastics.
Fiber-Optic-Bond 23, High Temp Epoxy Adhesive, Fast Cure, Low Visc, 2 Part, Fiber Optic Connectors has good impact and thermal shock resistance, and yields excellent low stress, pot-and-polish connections which do not piston during cycle tests. It is also resistant to water and weathering, vapors and gases, most petroleum products, and an extended range of organic and inorganic environments. Shorter cures at higher temperatures (e.g. 2 minutes at 120C or 1 minute at 150C) are also possible. An additional post-cure of 30 minutes at 150C is recommended when application temperatures higher than 150C are anticipated.
GENERAL PROPERTIES
| Components | 2 component - requires mixing |
| Mix Ratio by weight | 100:10 / Resin:Hardener |
| Benefits | Low viscosity
Thermal shock and impact resistant
Low stress connections
Color coded |
| Cure Type | Room temperature or Heat Cure |
| Operating Temperature | -60 to 175 C |
| Typical Applications | Fiber optic assembly, multimode and single mode connectors, small potting and sealing applications. |
| Appearance | (Unmixed) Light yellow
(cured) Reddish-amber |
UNCURED PROPERTIES:
| Viscosity @ 25 C | 2100 |
| Specific Gravity | 1.19 |
| Pot Life | 2 hours |
CURE SCHEDULE:
| 24 hours | @ 25C |
| 5 minutes | @ 100C |
CURED PROPERTIES:
| Glass Transition (Tg), ultimate, C | 120 |
| Hardness, Shore D | 85 |
| Refractive Index | 1.54 |
| Tensile Shear, alum to alum, psi | 2800 |
| Dielectric Strength | 15.7 kV/mm 400 kV/in |
GENERAL INFORMATION:
For safe handling information on this product, consult the Material Safety Data Sheet, (MSDS).
HOW TO USE:
1) Carefully clean and dry all surfaces to be bonded.
2) Apply Fiber-Optic-Bond 23, High Temp Epoxy Adhesive, Fast Cure, Low Visc, 2 Part, Fiber Optic Connectors completely mixed adhesive to the prepared surfaces, and gently press these surfaces together. Contact pressure is adequate for strong, reliable bonds; however, maintain contact until adhesive is completely cured.
3) Some separation of components is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use.
4) Some ingredients in this formulation provided may crystallize when subjected to low temperature storage. A gentle warming cycle of 52C for 30 minutes prior to mixing components may be necessary. Crystallized epoxy components do not react as well as liquid components and should be re-dissolved prior to use for best results.
AVAILABILITY:
This epoxy can be supplied in various different packages.
Loading... Please wait...